Code: 10145. We produce a biocompound consisting of a granulated polypropylene support with the addition of wood flour.

The wood flour PP granule is 100% recyclable. because, if collected separately, they can be used to produce the same products.

In the PP granule with wood flour the molding temperatures can vary from 160°C to 190°C. Higher temperatures tend to cause deterioration of the wood flour contained in the material.

Wood flour PP granule is sensitive to air humidity and tends to absorb (or disperse) water vapor when exposed to humidity (or dry environments) for long periods.

Before use, drying at 60-70°C for 5-6 hours is recommended.

Technical characteristics of PP granules with wood flour:

- Composition: PP 70% + Wood flour 30%

- Density: 0.993 gr./cm3

- Tensile modulus 1 mm/min: MPa 2500

- Tensile strength at break 5mm/min: MPa 24

- Tensile elongation at break 5mm/min: % 3

- Flexural modulus 2mm/min: MPa 2000

- Bending stress at 3.5% strain: MPa 41

- Impact resistance Izod serrated 23°C; 50%: KJ/m2 3

- Izod impact resistance without notch 23°C; 50%: KJ/m2 8

If you require further technical or commercial information you can contact our sales office.

Origin: Italy

Category: Biopolymers - PP - wood flour - recycling